Werkstoffvergleichstabelle I -
| Kurzname
|
W. Nr.
|
AISI
|
ASTM - UNS
|
AFNOR
|
Warenzeichen
|
Kg/dm3
|
| Cr + Ni
|
|
|
| X5 CrNi 18.10
|
1.4301
|
304
|
S 30400
|
Z 6 CN 18.09
|
8,00
|
| X 5 CrNi 18.12
|
1.4303
|
305
|
|
Z 8 CN 18.12
|
8,00
|
| X 10 CrNi S 18.9
|
1.4305
|
303
|
S 30300
|
Z 10 CNF 18.09
|
8,00
|
| X 2 CrNi 19.11
|
1.4306
|
304 L
|
S 30403
|
Z 3 CN 18.10
|
8,00
|
| X 12 CrNi 17.7
|
1.4310
|
301
|
S 30100
|
Z 11 CN 18.08
|
8,00
|
| X 2 CrNiN 18.10
|
1.4311
|
304 LN
|
S 30453
|
Z 3 CN 18.10 Az
|
8,00
|
| X 1 CrNi 25.21
|
1.4335
|
310 L
|
|
Z 1 CN 25.20
|
URANUS 65/SS25L
|
8,00
|
| X 1 CrNiSi 18.15
|
1.4361
|
|
S 30600
|
Z 1 CNS 17.15
|
URANUS S1/ANTINIT
|
8,00
|
| X 6 CrNiTi 18.10
|
1.4541
|
321
|
S 32100
|
Z 6 CNT 18.10
|
|
8,00
|
| X6CrNiNb 18.10
|
1.4550
|
347 (H)
|
S 34700
|
Z 6 CNNb 18.10
|
8,00
|
| Cr + Ni + Mo
|
|
| X 5 CrNiMo 17.12.2
|
1.4401
|
316
|
S 31600
|
Z 7 CND 17.11.02
|
8,00
|
| X 2 CrNiMo 17.13.2
|
1.4404
|
316 L
|
S 31603
|
Z 3 CND 18.12.2
|
8,00
|
| X 2 CrNiMoN 17.12.2
|
1.4406
|
316 LN
|
S 31653
|
Z 3 CND 17.11 Az
|
8,00
|
| X 2 CrNiMoN 17.13.3
|
1.4429
|
316 LN (Mo+)
|
(S 31653)
|
Z 3 CND 17.1 2 Az
|
8,00
|
| X 2 CrNiMo 18.14.3
|
1.4435
|
316 L (Mo+)
|
S 31609
|
Z 3 CND 18.14.03
|
8,00
|
| X 5 CrNiMo 17.13.3
|
1.4436
|
316 (Mo)
|
|
Z 6 CND 18.1 2.03
|
8,00
|
| X 2 CrNiMo 18.16.4
|
1.4438
|
31 7 L
|
S 31703
|
Z 3 CND 19.15.04
|
8,00
|
| X 2 CrNiMoN 17.13.5
|
1.4439
|
317 LN
|
S 31726
|
Z 3 CND 18.14.05 Az
|
8,00
|
| X 5 CrNiMo 17.13
|
1.4449
|
(317)
|
|
Z 6 CND 17.1 2.04
|
8,00
|
| X 1 CrNiMoN 25.25.2
|
1,4465
|
|
N08310/S31050
|
Z 2 CND 25.25 Az
|
8,00
|
| X 1 CrNiMoN 25.22.2
|
1.4466
|
|
S 31050
|
Z 2 CND 25.22 Az
|
8,00
|
| X 4 NiCrMoCuNb 20.18.2
|
1.4505
|
|
|
Z 5 NCDUNb 20.18
|
8,00
|
| X 5 NiCrMoCuTi 20.18
|
1.4506
|
|
|
Z 5 NCDUT 20.18
|
8,00
|
| X 5 NiCrMoCuN 25.20.6
|
1.4529
|
|
S31254 (?
|
|
(254SMO) 19.25 HMo
|
8,00
|
| X 1 NiCrMoCu 25.20.5
|
1.4539
|
904 L
|
N 08904
|
Z 2 NCDU 25.20
|
URANUS B6/2 RK 65
|
8,00
|
| X 1 NiCrMoCu 31.27.4
|
1,4563
|
|
N 08028
|
Z 1 NCDU 31.27.03
|
SANICRO 28
|
8,00
|
| X 6 CrNiMoTi 17.12.2
|
1.4571
|
316 Ti
|
S 31635
|
Z 6 CNDT 17.12
|
|
8,00
|
| X 3 CrNiMoTi 25.25
|
1.4577
|
|
|
Z 5 CNDT 25.24
|
8,00
|
| X 6 CrNiMoNb 17.12.2
|
1.4580
|
316 Cb/Nb
|
C31640
|
Z 6 CNDNb 17.12
|
8,00
|
| X 10 CrNiMoNb 18.12
|
1.4582
|
318
|
|
Z 6 CNDNb 17.13
|
8,00
|
| DUPLEX/SUPERDUPLEXα-γ
|
|
| X 2 CrNiN 23.4
|
1.4362
|
|
S 32304/S 39230
|
Z 3CN 23.04 Az
|
URANUS 35N/SAF 23.04
|
8,00
|
| X 2 CrNiMoN 25.7.4
|
1.4410
|
|
S 31260/S 39226
|
Z 3 CND 25.07 Az
|
URANUS 47N
|
8,00
|
| X 3 CrNiMoN 27.5.2
|
1.4460
|
329
|
S 32900
|
Z 5 CND 27.05 Az
|
SS44
|
8,00
|
| X 2 CrNiMoN 22.5.3
|
1.4462
|
(329 LN)/F 51
|
S 31803/S 39209
|
Z 3 CND 22.05 Az
|
URANUS 45N/SAF 22.05
|
8,00
|
| X 2 CrNiMoCuWN 25.7.4
|
1.4501
|
F 55
|
S 32760
|
|
ZERON 100
|
8,00
|
| X 2 CrNiMoCuN 25.6.3
|
1.4507
|
|
S 32550/S 32750
|
Z 3 CNDU 25.07 Az
|
URANUS 52N/SAF 25.07
|
8,00
|
| X 2 CrNiMnMoNbN 25.18.5.4
|
1.4565
|
|
S 24565
|
|
4565/DUPLEX + 6 Mo
|
8,00
|
| C°- 600℃- 1200℃
|
| X 10 CrAl 7
|
1.4713
|
|
|
Z 8 CA 7
|
SICROMAL 8
|
8,00
|
| X 10 CrSiAl 13
|
1.4724
|
|
|
Z 13 C 13
|
SICROMAL 9
|
8,00
|
| X10CrAI18
|
1.4742
|
442
|
S 44200
|
Z 12 CAS 18
|
SICROMAL 10
|
8,00
|
| X 18 CrN 28
|
1.4749
|
446
|
S 44600
|
Z 18 C 25
|
SICROMAL 11/4 C 54
|
8,00
|
| X 10 CrAlSi 24
|
1.4762
|
|
|
Z 12 CAS 25
|
SICROMAL 12
|
8,00
|
| X 20 CrNiSi 25.4
|
1.4821
|
327
|
|
Z 20 CNS 25.04
|
|
8,00
|
| X 15 CrNiSi 20.12
|
1.4828
|
302 B/ 309
|
S 30215/30900
|
Z 17 CNS 20.12
|
8,00
|
| X 6 CrNi 22.13
|
1.4833
|
309 (S)
|
S 30908
|
Z 15 CN 24.13
|
8,00
|
| X 15 CrNiSi 25.20
|
1.4841
|
310/314
|
S 31000/31400
|
Z 15 CNS 25.20
|
8,00
|
| X 12 CrNi 25.21
|
1.4845
|
310 (S)
|
S 31008
|
Z 8 CN 25.20
|
8,00
|
| X 12 NiCrSi 35.16
|
1.4864
|
330
|
N 08330
|
Z 20 NCS 33.16
|
INCOLOY DS
|
8,00
|
| X 10 NiCrAlTi 32.20
|
1.4876
|
|
N 08800
|
Z 10 NC 32.21
|
INCOLOY 800 (H/HT)
|
8,00
|
| X 12 CrNiTi 18.9
|
1.4878
|
321 H
|
S 32109
|
Z 6 CNT 18.12
|
|
8,00
|
| X 8 CrNiSiN 21.11
|
1.4893
|
|
S 30815
|
|
253 MA
|
8,00
|
| X 6 CrNiMo 17.13
|
1.4919
|
316 H
|
S 31609
|
Z 6 CND 17.12
|
|
8,00
|
| X 6 CrNi 18.11
|
1.4948
|
304 H
|
S 30409
|
Z 6 CN 18.11
|
8,00
|
| X 5 NiCrAlTi 31.20
|
1.4958
|
|
N 08810
|
Z 10 NC 32.21
|
INCOLOY 800 H
|
8,00
|
| X 8 NiCrAlTi 31.21
|
1.4959
|
|
N 08811
|
|
INCOLOY 800 HT
|
8,00
|
| Cr
|
|
|
| X 6 Cr 13
|
1.4000
|
410 S
|
S 41008
|
Z 8 C 12
|
8,00
|
| X 6 CrAl 13
|
1.4002
|
405
|
S 40500
|
Z 8 CA 12
|
8,00
|
| X 12 CrS13
|
1.4005
|
416
|
S 41600
|
Z 13 CF 13
|
8,00
|
| X 12 Cr 13
|
1.4006
|
410
|
S41000
|
Z 10 C 13
|
8,00
|
| X 6 Cr 17
|
1.4016
|
430
|
S 43000
|
Z 8 C 17
|
8,00
|
| X 20 Cr 13
|
1.4021
|
420
|
S 42000
|
Z 20 C 13
|
8,00
|
| X 15 Cr 13
|
1.4024
|
420 S
|
J 91201
|
Z 15 C 13
|
8,00
|
| X 30 Cr 13
|
1.4028
|
420
|
J 91153
|
Z 33 C 13
|
8,00
|
| X 46 Cr 13
|
1.4034
|
(420)
|
|
Z 44 C 14
|
8,00
|
| X 19 CrNi 17.2
|
1.4057
|
431
|
S 43100
|
Z 15 CN 16.02
|
8,00
|
| X14 CrMoS 17
|
1.4104
|
430 F
|
S 43020
|
Z 13 CF 17
|
8,00
|
| X 90 CrMoV 18
|
1.4112
|
440 B
|
S 44003
|
Z 90 CDV 18
|
8,00
|
| X 39 CrMo 17.1
|
1.4122
|
|
|
Z 38 CD 16.01
|
8,00
|
| X 105 Cr Mo 17
|
1.4125
|
440 C
|
S 44004/S 44025
|
Z 100 CD 17
|
8,00
|
| X 5 CrTi 1 7
|
1.4510
|
430 Ti
|
S 43036/S 43900
|
Z 4 CT 17
|
8,00
|
| X5 CrNiCuNb 16.4
|
1.4542/
1.4548
|
630
|
S17400
|
Z 7 CNU 17.04
|
17.4 PH
|
8,00
|
| X 7 CrNiAl 17.7
|
1.4568
|
631
|
S17700
|
Z 9 CNA 1 7.07
|
17.7 PH
|
8,00
|
Werkstoffvergleichstabelle II - 材料比较表II
| Kurzname
|
W. Nr.
|
ASTM - UNS
|
AFNOR
|
Warenzeichen
|
Kg/dm3
|
| Ni + Ni Legierungen
|
| Ni 99,2
|
2.4066
|
N 02200
|
Ni 99,2
|
NICKEL 200
|
8,90
|
| LC - Ni 99
|
2.4068
|
N 02201
|
LC - Ni 99
|
NICKEL 201
|
8,90
|
| NiCu 30 Fe
|
2.436
|
N 04400
|
Cu 30
|
MONEL 400
|
8,90
|
| NiCu 30 AI
|
2.4375
|
N 05500
|
Nu 30 AT
|
NICKEL K500
|
8,72
|
| NiCr 21 Mo 14 W
|
2.4602
|
N 06022
|
|
HASTELLOY C22
|
8,69
|
| NiCr 30 FeMo
|
2.4603
|
N 46030
|
|
HASTELLOY G30
|
8,22
|
| NiCr 23 Mo 16 Al
|
2.4605
|
N 06059
|
|
ALLOY 59
|
8,60
|
| NiMo 16 Cr 16 Ti
|
2.461
|
N 06455
|
|
HASTELLOY C4
|
8,82
|
| NiMo 28
|
2.4617
|
N 10665
|
|
HASTELLOY B2
|
9,27
|
| NiCr 22 Mo 6 Cu
|
2.4618
|
|
|
HASTELLOY G
|
8,36
|
| NiCr 22 Mo 7 Cu
|
2.4619
|
N 06985
|
|
HASTELLOY G3
|
8,30
|
| NiCr 20 Ti
|
2.4630/2.4951
|
N 06075
|
NC 20 T
|
NIMONIC 75
|
8,51
|
| NiCr 20 TiAl
|
2.4631/2.4952
|
N 07080
|
NiCr 20 TiA
|
NIMONIC 80A
|
8,37
|
| NiCr 20 Co 18 Ti
|
2.4632/2.4969
|
N 07090
|
NC 20 KTA
|
NIMONIC 90
|
8,18
|
| NiCr 25 FeAl
|
2.4633
|
|
|
ALLOY 602 CA
|
8,00
|
| NiCo 20 Cr 15 Mo Al Ti
|
2.4634
|
N13021
|
NCKD 20 ATV
|
NIMONIC 105
|
8,01
|
| NiCr 29 Fe
|
2.4642
|
N 06690
|
NC 30 Fe
|
ALLOY 690
|
8,20
|
| NiCr 20 CuMo
|
2.4660
|
N 08020
|
|
CARPENTER 20 Cb 3
|
8,02
|
| NiCr 23 Co 12 Mo
|
2.4663
|
N 06617
|
NC 22 KDA
|
INCONEL 617
|
8,55
|
| NiCr 22 Fe 18 Mo
|
2.4665/2.4603
|
N 06002
|
NC 22 FeD
|
HASTELLOY X
|
8,50
|
| NiCr 19 NbMo
|
2.4668
|
N 07718
|
NC 19 FeNb
|
INCONEL 718
|
8,35
|
| NiCr 15 Fe 7 TiAl
|
2.4669
|
N 07750
|
NiCr 15 Fe 7 TiA
|
INCONEL X - 750
|
8,37
|
| CoCr 28
|
2.4778
|
|
|
UMCO 50
|
8,10
|
| NiCr 15 Fe
|
2.4816
|
N 06600
|
NC 15 Fe
|
INCONEL600 8
|
8,50
|
| NiMo 16 Cr 15 W
|
2.4819
|
N 10276
|
NiMo 16 Cr 15
|
HASTELLOY C 276
|
9,13
|
| NiCr 23 Fe
|
2.4851
|
N 06601
|
NiCr 23 Fe
|
INCONEL 601
|
8,25
|
| NiCr 22 Mo 9 Nb
|
2.4856
|
N 06625
|
NC 22 DNb
|
INCONEL 625
|
8,63
|
| NiCr 21 Mo
|
2.4858
|
N 08825
|
NC 21 FeDU
|
INCOLOY 825
|
8,18
|
| Cu - Ni Kupfer - Nickel
|
| CuNi 10 Fe
|
2.0872
|
C 70600
|
CuNi 10 Fe 1 Mn
|
CUPRONICKEL 90/10
|
8,93
|
| CuNi 30 Fe
|
2.0882
|
C 71500
|
CuNi 30 Fe 1 Fe
|
CUPRONICKEL 70/30
|
8,93
|
| Ti - Titan
|
|
|
3.7025
|
R 50250
|
T 35
|
GRADE I (1)
|
4,50
|
|
|
3.7035
|
R 50400
|
T 40
|
GRADE II (2)
|
4,50
|
|
|
3.7055
|
R 50550
|
T 50
|
GRADE III (3)
|
4,50
|
|
|
3.7065
|
|
T 60
|
GRADE IV (4)
|
4,50
|
|
|
3.7164/3.7165
|
|
TA 6 V
|
GRADE V (5)
|
4,50
|
| Ti II Pb
|
3.7235
|
R 52400
|
|
GRADE VII (7)
|
4,50
|
| Ti Pb
|
3.7225
|
R 52250
|
|
GRADE XI (11)
|
4,50
|
主要材料0Cr18Ni9(304),00Cr19Ni10(304L),0Cr18Ni10Ti(321),0Cr17Ni12Mo2(316),00Cr17Ni14Mo2(316L),0Cr18Ni12Mo2Ti(1.4571),0Cr19Ni13Mo3(317),00Cr19Ni13Mo3(317L),0Cr18Ni11Nb(347),1Cr19Ni11Nb
(347H), 耐热不锈钢管0Cr25Ni20(310S),以及双相不锈钢管00Cr18Ni5Mo3Si2(S31500、3RE60),00Cr22Ni5Mo3N(S31803、SAF2205)等。
| 序号
|
中国
（GB）
|
日本
（JIS）
|
美国
（ASTM）
|
化学成份(wt%)
|
| C
|
Si
|
Mn
|
P
|
S
|
Ni
|
Cr
|
Other
|
| 1.
|
1Cr18Ni9Ti
|
.
|
.
|
≤0.12
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
8.00-10.00
|
17.00-19.00
|
Ti5(c-0.02)-0.80
|
| 2.
|
0Cr18Ni10Ti
|
SUS321
|
321,S32100
|
≤0.08
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
9.00-12.00
|
17.00-19.00
|
Ti≥5c%
|
| 3.
|
0Cr18Ni9
|
SUS304
|
304,S30400
|
≤0.07
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
8.00-11.00
|
17.00-19.00
|
.
|
| 4.
|
00Cr19Ni10
|
SUS304L
|
304L,S30403
|
≤0.030
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
8.00-10.00
|
18.00-20.00
|
.
|
| 5.
|
0Cr17Ni12Mo2
|
SUS316
|
316,S31600
|
≤0.08
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
10.00-14.00
|
16.00-18.50
|
Mo:2.00-3.00
|
| 6.
|
00Cr17Ni14Mo2
|
SUS316
|
L316L.S31603
|
≤0.030
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
12.00-15.00
|
16.00-18.00
|
Mo:2.00-3.00
|
| 7.
|
0Cr18Ni12Mo2Ti
|
.
|
.
|
≤0.08
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
11.00-14.00
|
16.00-19.00
|
Mo:1.80-2.50
|
| 8.
|
0Cr25Ni20
|
SUS310S
|
310S,S31008
|
≤0.08
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
19.00-22.00
|
24.00-26.00
|
.
|
| 9.
|
0Cr18Ni11Nb
|
SUS347
|
347,S34700
|
≤0.08
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
9.00-13.00
|
17.00-19.00
|
Nb≥100%
|
| 10.
|
00Cr18Ni5Mo3Si2
|
.
|
.
|
≤0.030
|
1.30-2.00
|
1.00-2.00
|
≤0.035
|
≤0.030
|
4.50-5.50
|
18.00-19.50
|
Mo:2.50-3.00
|
| 11.
|
1Cr18Ni19
|
SUS302
|
302,S30200
|
≤0.15
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
8.00-10.00
|
17.00-19.00
|
.
|
| 12.
|
0Cr13
|
SUS410S
|
410S
|
≤0.08
|
≤1.00
|
≤2.00
|
≤0.035
|
≤0.030
|
≤0.60
|
11.50-13.50
|
.
|
|
316（1.4401）和316L(1.4404/1.4432)与316Ti(1.4571)的比较
|
|
|
| 什么是316Ti(1.4571)？
316Ti不锈钢传统上被德国技师和用户用材料（Werkstoff）代码1.4571来划定。前者钢级别在英国标准（UK）中是320S31。
这个级别实质上是加钛稳定后的316型标准碳钢，原则上与304(1.4301)加钛稳定形成321 (1.4541)相似。钛的加入主要用来减少425-815℃温度加热后产生的晶间腐蚀（IC）。
晶间腐蚀（IC）
当奥氏体不锈钢在425-815℃温度范围内持续加热时，钢中的碳弥散到晶粒边界，沉积出铬碳化物。这个过程会从固熔物中带走铬，造成晶粒边界周围铬含量降低。这种状态下的钢称为敏化态钢。暴露于腐蚀性环境中时晶粒边界就会变得易于优先侵蚀。这种腐蚀类型成为晶间腐蚀，过去也称为焊接接头腐蚀。
由于钛的加入，钛的碳氮化物优于铬碳化物而形成，从而维持铬在整个钢结构中的恰当分布，进而减小了发生晶间腐蚀IC的危险。
结果是，在晶界附碳氮化物形成的区域，铬并没有消耗到可以在晶界区域发生局部腐蚀的程度。
减小晶间腐蚀IC侵蚀另外一种方法是减小碳含量到0.03%以下。实际上，用这种方法可以获得具有与316Ti (320S31/1.4571)相似的耐晶间腐蚀性的316级别。这是316L(316S11/1.4404 and 316S13/1.4432)型的基础。
316Ti可与316L互换吗？
在大多数情况下，两种级别可以互换，316L (316S11/1.4404)适于用到316Ti (320S31/1.4571)指定使用的地方。在室温的水性腐蚀的介质或环境中，指定316Ti优于316L没有任何实际的益处。在某些情况下，316L (1.4404 / 1.4432)级别也许是更好的选择。
机械性能
1.4571中钛的存在会对使机械强度有一定的提高，尤其是在600℃以上的高温时的强度，因此，选择1.4404作为这种条件下的替代品是一定要慎重。然而，相比1.4404 / 1.4432型，1.4571室温时的冲击性能较差。
切削加工性
由于钛碳氮化物粒子会导致较高的刀具磨损，也可能不会像1.4404 / 1.4432型那样易于冷成形或冷压，所以1.4571的切削加工性也会成为一个问题。
抛光性能
要求高标准的抛光表面时，1.4571中钛碳氮化物的存在也会产生问题。当钢在抛光过程中受到拉拔时，钛碳氮化物粒子会造成抛光表面“彗尾”条纹。这与1.4541(321)相似，并不推荐其用现已过时的BS1449Pt2的8号光亮机械抛光（现在已被BSEN 10088:2-1995平整件1P/2P取代）
耐腐蚀性
尽管通常认为一般的耐腐蚀性相似，也有一些证据表明，相比1.4404 / 1.4432 型，1.4571 型耐点蚀和应力腐蚀性差一些。钛稳定1.4571级别也易于在焊接热影响区发生刀状腐蚀，非常接近于固态钢母体中碳氮化物发生重熔的熔化区。
可焊接性
4571和1.4404 / 1.4432的可焊接性通常认为相似，但两种级别都不会更易于焊接或比对方更优越。铌稳定填充物（焊接消耗物）可用来焊接1.4571，尤其是在高温焊接强度比较重要的地方。在其它条件下，316L填充料应该使焊接金属耐水腐蚀性与母体1.4571 ’316Ti’材料相匹配。
标准
BS970-1:1996机械或联合工程目的的焊接钢 一般的检查和测试程序和指定要求的碳、碳锰、合金和不锈钢。
BS 1449:Part 2:1983 钢片、板和带材 不锈和耐热钢片、板和带材规格。
BS EN 10088-2:2005 不锈钢 通用耐腐蚀片/板材钢的技术转换条件。
BS EN 10088-3:2005不锈钢 通用耐腐蚀半成品邦、条、线材，断面光亮钢产品的技术转换条件。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
德国DIN标准耐热铸钢[DIN 17465—1993]
a.耐热铸钢的钢号与化学成分，见表1。
表1 耐热铸钢的钢号与化学成分（质量分数）（%）
| 钢 号
|
材料号
|
C
|
Si
|
Mn
|
P
≤
|
S
≤
|
Cr
|
Ni
|
其他
|
| GX30CrSi6
|
1.4710
|
0.20～0.35
|
1.0～2.5
|
0.5～1.0
|
0.035
|
0.030
|
6.0～8.0
|
—
|
—
|
| GX40CrSi13
|
1.4729
|
0.30～0.45
|
1.0～2.5
|
0.5～ 1.0
|
0.035
|
0.030
|
12.0～14.0
|
—
|
—
|
| GX40CrSi17
|
1.1740
|
0.30～0.45
|
1.0～2.5
|
0.5～1.0
|
0.035
|
0.030
|
16.0～18.0
|
—
|
—
|
| GX40CrSi23
|
1.4745
|
0.30～0.45
|
1.0～2.5
|
0.5～1.0
|
0.035
|
0.030
|
22.0～24.0
|
—
|
—
|
| GX40CrSi29
|
1.4776
|
0.30～0.45
|
1.0～2.5
|
0.5～1.0
|
0.035
|
0.030
|
27.0～30.0
|
—
|
—
|
| GX130CrSi29
|
1.4777
|
1.20～1.40
|
1.0～2.5
|
0.5～1.0
|
0.035
|
0.030
|
27.0～30.0
|
—
|
—
|
| GX40CrNiSi27-4
|
1.4823
|
0.35～0.50
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
25.0～28.0
|
3.5～5.5
|
—
|
| GX25CrNiSi18-9
|
1.4825
|
0.15～0.30
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
17.0～19.0
|
8.0～10.0
|
—
|
| GX40CrNiSi22-9
|
1.4826
|
0.30～0.50
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
21.0～23.0
|
9.0～11.0
|
—
|
| GX25CrNiSi20-14
|
1.4832
|
0.15～0.30
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
19.0～21.0
|
13.0～15.0
|
—
|
| GX40CrNiSi25-12
|
1.4837
|
0.30～0.50
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
24.0～26.0
|
11.0～14.0
|
—
|
| GX40CrNiSi25-20
|
1.4848
|
0.30～0.50
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
24.0～26.0
|
19.0～21.0
|
—
|
| GX40CrNiSi38-18
|
1.4865
|
0.30～0.50
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
17.0～19.0
|
36.0～39.0
|
—
|
| GX40CrNiSi35-25
|
1.4857
|
0.30～0.50
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
24.0～26.0
|
34.0～36.0
|
—
|
| GX30CrNiSiNb24-24
|
1.4855
|
0.25～0.40
|
0.5～2.0
|
≤1.5
|
0.035
|
0.030
|
23.0～25.0
|
23.0～25.0
|
Nb1.2～1.8
|
| GX40CrNiSiNb38-18
|
1.4849
|
0.30～0.50
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
17.0～19.0
|
36.0～39.0
|
Nb1.2～1.8
|
| GX40CrNiSiNb35-25
|
1.4852
|
0.35～0.45
|
1.0～2.5
|
≤1.5
|
0.035
|
0.030
|
24.0～26.0
|
33.0～35.0
|
Nb0.8～1.8
|
| G-CoCr28
|
2.4778
|
0.10～0.20
|
0.5～1.5
|
≤1.5
|
0.035
|
0.030
|
27.0～30.0
|
—
|
Co18.0～52.0
|
| G-NiCr28W
|
2.4879
|
0.35～0.50
|
0.5～2.0
|
≤1.5
|
0.035
|
0.030
|
27.0～30.0
|
47.0～50.0
|
W4.0～5.5
|
b.耐热铸钢的室温力学性能，见表2。
表2 耐热铸钢的室温力学性能
| 钢 号
|
材料号
|
铸钢件状态
|
力学性能（不小于）
|
硬 度≤HBS30
|
| σ0.2 /MPa
|
σb /MPa
|
δ5(%)
|
| 铁素体形
|
| GX30CrSi6
|
1.4710
|
800～850oC退火
|
—
|
—
|
—
|
300
|
| GX40CrSi13
|
1.4729
|
300
|
| GX40CrSi17
|
1.1740
|
300
|
| GX40CrSi23
GX40CrSi29
GX130CrSi29
|
1.4745
1.4776
1.4777
|
铸态
|
—
|
—
|
—
|
—
|
| 铁素体－奥氏体型
|
| GX40CrNiSi27-4
|
1.4823
|
铸态
|
—
|
—
|
—
|
—
|
| 奥氏体型
|
| GX25CrNiSi18-9
|
1.4825
|
铸态
|
230
|
440
|
15
|
—
|
| GX40CrNiSi22-9
|
1.4826
|
230
|
440
|
8
|
| GX25CrNiSi20-14
|
1.4832
|
230
|
440
|
10
|
| GX40CrNiSi25-12
|
1.4837
|
230
|
440
|
7
|
| GX40CrNiSi25-20
|
1.4848
|
230
|
440
|
6
|
| GX40CrNiSi38-18
|
1.4865
|
230
|
400
|
5
|
| GX40CrNiSi35-25
|
1.4857
|
230
|
440
|
5
|
| GX30CrNiSiNb24-24
|
1.4855
|
230
|
440
|
5
|
| GX40CrNiSiNb38-18
|
1.4849
|
220
|
400
|
5
|
| GX40CrNiSiNb35-25
|
1.4852
|
220
|
400
|
5
|
| GCoCr28
|
2.4778
|
—
|
—
|
—
|
| GNiCr28W
|
2.4879
|
—
|
—
|
—
|
c.耐热铸钢的高温力学性能，见表3。
表3 耐热铸钢的高温力学性能
| 钢 号
|
材料号
|
下列温度时1％－10000h的蠕变强度／MPa
|
最高工作温度/oC
|
| 600oC
|
700oC
|
800oC
|
900oC
|
1000oC
|
1100oC
|
| GX30CrSi6
GX40CrSi13
GX40CrSi17
GX40CrSi23
GX40CrSi29
GX130CrSi29
|
1.4710
1.4729
1.1740
1.4745
1.4776
1.4777
|
19.5
22
22
26
26
—
|
8
9
9
11
11
—
|
2.5
2.5
3.5
5
5
—
|
—
1
1
1.5
1.5
—
|
—
—
—
—
—
—
|
—
—
—
—
—
—
|
750
850
900
1050
1150
1100
|
| GX40CrNiSi27-4
|
1.4823
|
—
|
21
|
9
|
4
|
1.5
|
—
|
1100
|
| GX25CrNiSi18-9
GX40CrNiSi22-9
GX25CrNiSi20-14
GX40CrNiSi25-12
GX40CrNiSi25-20
|
1.4825
1.4826
1.4832
1.4837
1.4848
|
78
82
82
—
—
|
44
46
46
50
66
|
22
23
23
26
36
|
9.5
10
10
12.5
17
|
—
—
—
5.5
7
|
—
—
—
—
—
|
900
950
950
1050
1100
|
| GX40CrNiSi38-18
GX40CrNiSi35-25
|
1.4865
1.4857
|
—
—
|
55
70
|
32
40
|
16
20
|
6.5
8
|
—
2
|
1050
1100
|
| GX30CrNiSiNb24-24
GX40CrNiSiNb38-18
GX40CrNiSiNb35-25
|
1.4855
1.4849
1.4852
|
—
—
—
|
80
60
72
|
46
38
41
|
22
20
22
|
7.5
8
9
|
—
—
2
|
1050
1000
1100
|
| GCoCr28
GNiCr28W
|
2.4778
2.4879
|
—
—
|
70
70
|
34
41
|
16
22
|
6
10
|
—
4
|
1100
1150
|
（2） 德国DIN标准铁素体热强铸钢[DIN 17245—1987]
a.铁素体热强铸钢的钢号与化学成分，见表4。
表4 铁素体热强铸钢的钢号与化学成分（质量分数）（%）
| 钢 号
|
材料号
|
C
|
Si
|
Mn
|
P
≤
|
S
≤
|
Cr
|
Ni
|
其他
|
| GS-C25
|
1.0619
|
01.8～0.23
|
0.30～0.60
|
0.50～0.80
|
0.020
|
0.015
|
≤0.30
|
—
|
—
|
| GS-22Mo4
|
1.5419
|
0.18～0.23
|
0.30～0.60
|
0.50～0.80
|
0.020
|
0.015
|
≤0.30
|
—
|
Mo0.35～0.45
|
| GS-17CrMo5 5
|
1.7357
|
0.15～0.20
|
0.30～0.60
|
0.50～0.80
|
0.020
|
0.015
|
1.00～1.50
|
—
|
Mo0.45～0.55
|
| GS-18CrMo9 10
|
1.7379
|
0.15～0.20
|
0.30～0.60
|
0.50～0.80
|
0.020
|
0.015
|
2.00～2.50
|
—
|
Mo0.90～1.10
|
| GS-17CrMoV5 11
|
1.7709
|
0.15～0.20
|
0.30～0.60
|
0.50～0.80
|
0.020
|
0.015
|
1.20～1.50
|
—
|
Mo0.90～1.10
V0.20～0.30
|
| G-XCrNi12
|
1.4107
|
0.06～0.10
|
0.10～0.40
|
0.50～0.80
|
0.030
|
0.020
|
11.5～12.5
|
0.80～1.50
|
Mo≤0.50
N≤0.05
|
| G-XCrMoV12 1
|
1.4931
|
0.20～0.26
|
0.10～0.40
|
0.50～0.80
|
0.030
|
0.020
|
11.3～12.2
|
0.70～1.00
|
Mo1.00～1.20
V 0.25～0.35
（W≤0.50）
|
b.铁素体热强铸钢的力学性能，见表5。
表5 铁素体热强铸钢的力学性能
| 钢 号
|
材料号
|
σb /MPa
|
下列温度时的σ0.2 /MPa
|
δ5
>=
(%)
|
A KV
/>J
|
| 20oC
|
200oC
|
300oC
|
350oC
|
400oC
|
450oC
|
500oC
|
550oC
|
| GS-C25
|
1.0619
|
440～590
|
245
|
175
|
145
|
135
|
130
|
125
|
|
|
22
|
27
|
| GS-22Mo4
|
1.5419
|
440～590
|
245
|
190
|
165
|
155
|
150
|
145
|
135
|
|
22
|
27
|
| GS-17CrMo5 5
|
1.7357
|
490～640
|
315
|
255
|
230
|
215
|
205
|
190
|
180
|
160
|
20
|
27
|
| GS-18CrMo9 10
|
1.7379
|
590～740
|
400
|
355
|
345
|
330
|
315
|
305
|
280
|
240
|
18
|
40
|
| GS-17CrMoV5 11
|
1.7709
|
590～780
|
440
|
385
|
365
|
350
|
335
|
320
|
300
|
260
|
15
|
27
|
| G-XCrNi12
|
1.4107
|
540～690
|
355
|
275
|
265
|
260
|
255
|
|
|
|
18
|
35
|
| G-XCrMoV12 1
|
1.4931
|
740～880
|
385
|
450
|
430
|
410
|
390
|
370
|
340
|
290
|
15
|
21
|
| 对应产品名：奥氏体铸铁
|
| 标准对照表：
|
|
|
| 标准内容：
|
| 片状石墨奥氏体铸铁的牌号与化学成分（质量分数）（％）
| ding=0
width="100%" border=1> 牌号
|
材料号
W-Nr.
|
C
|
Si
|
Mn
|
Cr
|
Ni
|
Cu
|
| GGL-NiMn137
|
0.6652
|
≤3.0
|
1.5~3.0
|
6.0~7.0
|
≤0.2
|
12.0~14.0
|
-
|
| GGL-NiCuCr1562
|
0.6655
|
≤3.0
|
1.0~2.8
|
0.5~1.5
|
1.0~2.5
|
13.5~17.5
|
5.5~7.5
|
| GGL-NiCuCr1563
|
0.6656
|
≤3.0
|
1.0~2.8
|
0.5~1.5
|
2.5~3.5
|
13.5~17.5
|
5.5~7.5
|
| GGL-NiCr202
|
0.6660
|
≤3.0
|
1.0~2.8
|
0.5~1.5
|
1.0~2.5
|
18.0~22.0
|
-
|
| GGL-NiCr203
|
0.6661
|
≤3.0
|
1.0~2.8
|
0.5~1.5
|
2.5~3.5
|
18.0~22.0
|
-
|
| GGL-NiSiCr2053
|
0.6667
|
≤2.5
|
3.5~5.5
|
0.5~1.5
|
1.5~4.5
|
18.0~22.0
|
-
|
| GGL-NiCr303
|
0.6676
|
≤2.5
|
1.0~2.0
|
0.5~0.8
|
2.5~3.5
|
28.0~32.0
|
-
|
| GGL-NiSiCr3055
|
0.6680
|
≤2.5
|
5.0~6.0
|
0.5~1.5
|
4.5~5.5
|
29.0~32.0
|
-
|
片状石墨奥氏体铸铁力学性能的补充数据
| ding=0
width="100%" border=1> 牌号
|
材料号
|
抗拉强度
σb≥/Mpa
|
抗压强度
σbc≥/Mpa
|
伸长率
δ（％）
|
弹性模量
E/Mpa
|
硬度
HBS
|
| GGL-NiMn137
|
0.5652
|
140~220
|
630~840
|
-
|
70~90
|
120~150
|
| GGL-NiCuCr1562
|
0.5655
|
170~210
|
700~840
|
2
|
85~105
|
120~215
|
| GGL-NiCuCr1563
|
0.6656
|
190~240
|
860~1100
|
12
|
98~113
|
150~250
|
| GGL-NiCr202
|
0.6660
|
170~210
|
700~840
|
23
|
85~105
|
120~215
|
| GGL-NiCr203
|
0.6661
|
190~240
|
860~1100
|
12
|
98~113
|
160~250
|
| GGL-NiSiCr2053
|
0.6667
|
190~280
|
-
|
23
|
|
140~250
|
| GGL-NiCr303
|
0.6676
|
190~240
|
700~910
|
13
|
98~113
|
120~215
|
| GGL-NiSiCr3055
|
0.6680
|
170~240
|
560
|
-
|
105
|
150~210
|
球状石墨奥氏体铸铁的牌号与化学成份（质量分数）（％）
| ding=0
width="87%" border=1> 牌号
|
材料号
W-Nr.
|
C
|
Si
|
Mn
|
Cr
|
Ni
|
| GGG-NiMn137
|
0.7652
|
≤3.0
|
2.0~3.0
|
6.0~7.0
|
-
|
12.0~14.0
|
| GGG-NiCrNb202
|
0.7659
|
≤3.0
|
1.5~2.4
|
0.5~1.5
|
1.5~2.5
|
18.0~22.0
|
| GGG-NiCr202
|
0.7660
|
≤3.0
|
1.5~3.0
|
0.5~1.5
|
1.0~2.5
|
18.0~22.0
|
| GGG-NiCr203
|
0.7661
|
≤3.0
|
1.5~3.0
|
0.5~1.5
|
2.5~3.5
|
18.0~22.0
|
| GGG-NiSiCr2052
|
0.7665
|
≤3.0
|
4.5~5.5
|
0.5~1.5
|
1.0~2.5
|
18.0~22.0
|
| GGG-Ni22
|
0.7670
|
≤3.0
|
1.0~3.0
|
1.5~2.5
|
-
|
21.0~24.0
|
| GGG-NiMn234
|
0.7673
|
≤2.6
|
1.5~2.5
|
4.0~4.5
|
-
|
22.0~24.0
|
| GGG-NiCr303
|
0.7676
|
≤2.6
|
1.5~2.5
|
0.5~1.5
|
2.5~3.5
|
28.0~32.0
|
| GGG-NiCr301
|
0.7677
|
≤2.6
|
1.5~3.0
|
0.5~1.5
|
1.0~1.5
|
28.0~32.0
|
| GGG-NiSiCr3052
|
0.7679
|
≤2.6
|
4.0~6.0
|
0.5~1.5
|
1.5~2.5
|
29.0~32.0
|
| GGG-NiSiCr3055
|
0.7680
|
≤2.6
|
4.0~6.0
|
0.5~1.5
|
4.5~5.5
|
28.0~32.0
|
| GGG-Ni35
|
0.7683
|
≤2.4
|
1.5~3.0
|
0.5~1.5
|
.-
|
34.0~36.0
|
| GGG-NiCr353
|
0.7685
|
≤2.4
|
1.53.0
|
0.51.5
|
2.03.0
|
34.0~36.0
|
| GGG-NiSiCr3552
|
0.7688
|
≤2.0
|
4.06.0
|
0.51.5
|
1.52.5
|
34.0~36.0
|
球状石墨奥氏体铸铁力学性能的补充数据
| ding=0
width="100%" border=1> 牌号
|
材料号
|
抗拉强度
σb≥/Mpa
|
抗压强度
σbc≥/Mpa
|
伸长率
δ（％）
|
弹性模量
E/Mpa
|
冲击吸收功
AKV/J
|
硬度
HBS
|
| GGG-NiMn137
|
0.7652
|
390~470
|
210~260
|
15~18
|
140~150
|
-
|
120~150
|
| GGG-NiCrNb202
|
0.7660
|
370~480
|
210~250
|
7~12
|
112~130
|
14~27
|
140~200
|
| GGG-NiCr202
|
0.7653
|
370480
|
210~250
|
8~12
|
112~130
|
14~27
|
140~200
|
| GGG-NiCr203
|
0.7661
|
370~500
|
210~260
|
7~15
|
112~133
|
12
|
150~255
|
| GGG-NiSiCr2052
|
0.7665
|
370~440
|
210~260
|
10~18
|
-
|
-
|
180~230
|
| GGG-Ni22
|
0.7670
|
370~450
|
170~250
|
20~40
|
85~112
|
21~33
|
130~170
|
| GGG-NiMn234
|
0.7673
|
440~480
|
210~240
|
25~45
|
120~140
|
24~34
|
150~180
|
| GGG-NiCr303
|
0.7677
|
370~450
|
210~270
|
13~18
|
112~130
|
16
|
130~190
|
| GGG-NiCr301
|
0.7676
|
379~480
|
210~260
|
7~18
|
92~105
|
8
|
140~200
|
| GGG-NiSiCr3052
|
0.7679
|
380~500
|
210~270
|
10~20
|
130~150
|
10~16
|
130~170
|
| GGG-NiSiCr3055
|
0.7680
|
390~500
|
240~310
|
1~4
|
91
|
-
|
170~250
|
| GGG-Ni35
|
0.7683
|
370~420
|
210~240
|
20~40
|
112~140
|
20
|
130~180
|
| GGG-NiCr353
|
0.7685
|
370~450
|
210~290
|
7~10
|
112~123
|
7
|
140~190
|
| GGG-NiSiCr3552
|
0.7688
|
370~500
|
200~290
|
10~20
|
110~145
|
12~19
|
130~170
|
|
|
| 对应产品名：不锈、耐蚀铸钢
|
| 标准对照表：
|
|
|
| 标准内容：
|
| (1)德国DIN标准不锈、耐蚀铸钢[DIN 17445—1984]
a.不锈、耐蚀铸钢的钢号与化学成分，见表5-58。
表5-58 锈、耐蚀铸钢的钢号与化学成分（质量分数）（%）
| 钢 号
|
材料号
W-Nr.
|
C
|
Si
|
Mn
|
P
≤
|
S
≤
|
Cr
|
Ni
|
Mo
|
其他
|
| 铁素（马氏体）体型
|
| G-X8CrNi13
|
1.4008
|
0.06~0.12
|
≤1.00
|
≤1.00
|
0.045
|
0.030
|
12.00~13.50
|
1.00~2.00
|
≤1.00
|
—
|
| G-X20Cr14
|
1.4027
|
0.16~0.23
|
≤1.00
|
≤1.00
|
0.045
|
0.030
|
12.00~14.50
|
≤1.00
|
—
|
—
|
| G-X22CrNi17
|
1.4059
|
0.20~0.27
|
≤1.00
|
≤1.00
|
0.045
|
0.030
|
16.00~18.00
|
1.00~2.00
|
—
|
—
|
| G-X5CrNi13 4
|
1.4313
|
≤0.07
|
≤1.00
|
≤1.50
|
0.025
|
0.025
|
12.00~13.50
|
3.50~5.00
|
≤0.70
|
—
|
| 奥氏体型
|
| G-X6CrNi18 9
|
1.4308
|
≤0.07
|
≤2.00
|
≤1.50
|
0.045
|
0.030
|
18.00~20.00
|
9.00~11.00
|
—
|
—
|
| G-X5CrNiNb18 9
|
1.4552
|
≤0.06
|
≤1.50
|
≤1.50
|
0.045
|
0.030
|
18.00~20.00
|
9.00~11.00
|
—
|
Nb≥8×C
|
| G-X5CrNiMoNb18 10
|
1.4581
|
≤0.06
|
≤1.50
|
≤1.50
|
0.045
|
0.030
|
18.00~20.00
|
10.50~12.50
|
2.00~2.50
|
Nb≥8×C
|
| G-X6CrNiMo18 10
|
1.4408
|
≤0.07
|
≤1.50
|
≤1.50
|
0.045
|
0.030
|
18.00~20.00
|
10.00~12.00
|
2.00~3.00
|
—
|
| G-X3CrNiMoN17 13 9
|
1.4439
|
≤0.04
|
≤1.00
|
≤1.50
|
0.045
|
0.030
|
16.50~18.50
|
12.50~14.50
|
4.00~4.50
|
N0.12~0.22
|
b.不锈、耐蚀铸钢的热处理与力学性能，见表5-59。
表5-59 不锈、耐蚀铸钢的热处理与力学性能
| 钢 号
|
材料号
W-Nr
|
热处理
|
力学性能（不小于）
|
| 退火温度
/℃
|
淬火温度/
℃及冷却
|
回火温度/℃或
去应力温度/℃
|
状态
|
σ0.2
/MPa
|
σb
/MPa
|
δ5
(%)
|
AKV
/J
|
硬度
HBS
|
| 铁素（马氏体）体型
|
| G-X8CrNi13
|
1.4008
|
700~750
|
1000~1050
空冷
|
650~720
300~350
|
调质
退火
|
590~790
—
|
440
—
|
25
—
|
27
—
|
170~240
170~240
|
| G-X20Cr14
|
1.4027
|
750~800
|
1000~1050
空冷
|
650~750
300~350
|
调质
退火
|
590~790
—
|
440
—
|
12
—
|
—
—
|
170~240
170~240
|
| G-X22CrNi17
|
1.4059
|
700~750
|
1000~1050
空冷
|
600~700
300~350
|
调质
退火
|
780~980
—
|
590
—
|
4
—
|
—
—
|
230~300
200~270
|
| G-X5CrNi13 4
|
1.4313
|
750~800
|
1000~1050
空冷
|
580~620
500~540
|
调质
退火
|
760~960
900~1100
|
590
—
|
15
12
|
50
35
|
240~300
280~350
|
| 奥氏体型
|
| G-X6CrNi18 9
|
1.4308
|
—
|
1050~1100
空，水冷
|
300~350
|
—
|
440~640
|
175
|
20
|
60
|
130~200
|
| G-X5CrNiNb18 9
|
1.4552
|
—
|
1050~1100
空，水冷
|
400~450
|
—
|
440~640
|
175
|
20
|
35
|
130~200
|
| G-X5CrNiMoNb18 9
|
1.4581
|
—
|
1050~1100
空，水冷
|
400~450
|
—
|
440~640
|
185
|
20
|
35
|
130~200
|
| G-X6CrNiMo18 10
|
1.4408
|
—
|
1050~1100
空，水冷
|
300~350
|
—
|
440~640
|
185
|
20
|
60
|
130~200
|
| G-X3CrNiMoNb17 13 5
|
1.4439
|
—
|
1050~1100
空，水冷
|
—
|
—
|
490~690
|
210
|
20
|
50
|
130~200
|
（2）德国DIN标准医疗器械用不锈铸钢[DIN 17442—1977]
a.医疗器械用不锈铸钢的钢号与化学成分，见表5-60。
表5-60 医疗器械用不锈铸钢的钢号与化学成分
| 钢 号
|
材料号
W-Nr.
|
C
|
Si
|
Mn
|
P
≤
|
S
≤
|
Cr
|
Mo
|
其他
|
| X20Cr13
|
1.4021
|
0.17~0.22
|
≤1.0
|
≤1.0
|
0.045
|
0.030
|
12.0~14.0
|
|
|
| X38CrMoV15
|
1.4117
|
0.35~0.40
|
≤1.0
|
≤1.0
|
0.045
|
0.030
|
14.0~15.0
|
0.40~0.60
|
V0.10~0.15
|
| G_X20CrMo13
|
1.4120
|
0.17~0.22
|
≤1.0
|
≤1.0
|
0.045
|
0.030
|
12.0~14.0
|
0.90~1.30
|
Ni≤1.0
|
| G_X35CrMo17
|
1.4122
|
0.33~0.43
|
≤1.0
|
≤1.0
|
0.045
|
0.030
|
15.5~17.5
|
0.90~1.00
|
Ni≤1.0
|
b.医疗器械用不锈铸钢的力学性能，见表5-61。
表5-61 医疗器械用不锈铸钢的力学性能
| 钢 号
|
材料号
|
铸件直径（d）
或壁厚（e）/mm
|
力学性能（不小于）
|
| σ0.2/MPa
|
σb/MPa
|
δ5(%)
|
| X20Cr13
|
1.4021
|
d ≤40；e≤30
|
650~850
|
500
|
10
|
| X38CrMoV15
|
1.4117
|
d ≤40；e≤5
|
≤900
|
—
|
—
|
| G-X20CrMo13
|
1.4120
|
d ≤40；e≤5
|
≤800
|
—
|
—
|
| G-X35CrMo17
|
1.4122
|
d ≤40；e≤5
|
≤950
|
—
|
—
|
(3) 德国非标准不锈、耐蚀铸钢
a.非标准不锈、耐蚀铸钢的钢号与化学成分，见表5-62。
表5-62 非标准不锈、耐蚀铸钢的钢号与化学成分（质量分数）（%）
| 钢号
|
材料号
W-Nr.
|
C
|
Si
|
Mn
|
P
≤
|
S
≤
|
Cr
|
Ni
|
Mo
|
其他
|
| G-X70Cr29
|
1.4085
|
0.50
~0.90
|
≤2.00
|
≤1.00
|
0.045
|
0.030
|
27.00~29.00
|
—
|
—
|
—
|
| C-X120Cr29
|
1.4086
|
0.90
~1.30
|
≤2.00
|
≤1.00
|
0.045
|
0.030
|
27.00~30.00
|
—
|
—
|
—
|
| G-X10CrMo13
|
1.4106
|
0.08
~0.13
|
≤1.00
|
≤1.00
|
0.045
|
0.030
|
11.50~13.50
|
0.50~1.00
|
0.40~0.60
|
—
|
| G-X70CrMo29 2
|
1.4136
|
0.50
~0.90
|
≤2.00
|
≤1.00
|
0.045
|
0.030
|
27.00~30.00
|
—
|
2.00~2.50
|
—
|
| G-X120CrMo29 2
|
1.4138
|
0.90
~0.30
|
≤2.00
|
≤1.00
|
0.045
|
0.030
|
27.00~29.00
|
—
|
2.00~2.50
|
—
|
| G-X2CrNi18 9
|
1.4306
|
≤0.03
|
≤1.50
|
≤1.50
|
0.045
|
0.030
|
17.00~20.00
|
9.00~12.00
|
—
|
—
|
| G-X10CrNi18 8
|
1.4312
|
≤0.12
|
≤2.00
|
≤1.50
|
0.045
|
0.030
|
17.00~19.50
|
8.00~10.00
|
—
|
—
|
| G-X40CrNi27 4
|
1.4340
|
0.30
~0.50
|
≤2.00
|
≤1.50
|
0.045
|
0.030
|
26.00~28.00
|
3.50~5.50
|
—
|
—
|
| G-X8CrNi26 7
|
1.4347
|
≤0.08
|
≤1.50
|
≤1.50
|
0.045
|
0.030
|
25.00~27.00
|
5.50~7.50
|
—
|
—
|
| G-X2CrNiMo18 10
|
1.4404
|
≤0.03
|
≤1.50
|
≤1.50
|
0.045
|
0.030
|
17.00~20.00
|
10.00~13.00
|
2.00~3.00
|
—
|
| G-X5CrNiMo16 5
|
1.4405
|
≤0.07
|
≤1.00
|
≤1.00
|
0.035
|
0.025
|
15.50~16.50
|
4.50~6.00
|
0.50~2.00
|
—
|
| G-X10CrNiMo18 9
|
1.4410
|
≤0.12
|
≤2.00
|
≤1.50
|
0.045
|
0.030
|
17.00~19.50
|
9.00~11.00
|
2.00~2.50
|
—
|
| G-X6CrNiMo18 12
|
1.4437
|
≤0.07
|
≤2.00
|
≤2.00
|
0.045
|
0.030
|
16.50~17.50
|
11.50~13.50
|
2.50~3.00
|
—
|
| G-X2CrNiMoN17 13 4
|
1.4446
|
≤0.03
|
0.60
~1.00
|
0.30
~0.60
|
0.030
|
0.020
|
16.50~17.50
|
13.00~14.00
|
4.30~4.80
|
N0.13~0.17
|
| G-X6CrNiMo17 13
|
1.4448
|
≤0.07
|
≤1.00
|
≤2.00
|
0.045
|
0.030
|
16.00~18.00
|
12.50~14.50
|
4.00~5.00
|
—
|
| G-X6CrNiMo24 8 2
|
1.4463
|
≤0.07
|
≤1.50
|
≤1.50
|
0.045
|
0.030
|
23.00~25.00
|
7.00~8.50
|
2.00~2.50
|
—
|
| G-X2CrNiMoN25 25
|
1.4465
|
≤0.03
|
≤1.00
|
≤2.00
|
0.045
|
0.030
|
24.00~26.00
|
22.00~25.00
|
2.00~2.50
|
N0.08~0.16
|
| G-X2NiCrMoCuN20 18
|
1.4531
|
≤0.03
|
0.30
~0.50
|
0.30
~0.60
|
0.030
|
0.020
|
17.00~18.50
|
19.00~21.00
|
2.10~2.40
|
Cu1.80~2.20
N0.10~0.17
|
| G-X2NiCrMoCuN25 20
|
1.4536
|
≤0.03
|
≤1.00
|
≤1.00
|
0.045
|
0.030
|
19.00~21.00
|
24.00~26.00
|
2.50~3.50
|
Cu1.50~2.20
N0.10~0.17
|
| G-NiMo16CrW
|
2.4537
|
≤0.10
|
≤1.00
|
≤1.00
|
0.045
|
0.030
|
14.00~18.00
|
≥52.00
|
15.00~18.00
|
W3.0~5.0
Cu≤0.50
Fe≤7.00
|
| G-X10CrNiMoNb18 12
|
1.4583
|
≤0.10
|
≤1.00
|
≤2.00
|
0.045
|
0.030
|
16.50~18.50
|
12.00~14.50
|
2.50~3.00
|
Nb≥8× C
|
| G-X7CrNiMoCuNb18 18
|
1.4585
|
≤0.08
|
≤1.50
|
≤2.00
|
0.045
|
0.030
|
16.50~18.50
|
19.00~21.00
|
2.00~2.50
|
Nb≥8× C
Cu1.80~2.40
|
| G-NiMo30
|
2.4810
|
≤0.05
|
≤0.50
|
≤1.00
|
0.030
|
0.015
|
≤1.00
|
≥ 62.00
|
26.00~30.00
|
Co≥2.5
V≤0.60
Cu≤0.50
Fe4.0~7.0
|
b. 非标准不锈、耐蚀铸钢的热处理与力学性能，见表5-63
表5-63 非标准不锈、耐蚀铸钢的热处理与力学性能
| 钢 号
|
材料号
W-Nr
|
热处理
|
力学性能（不小于）
|
| 退火温度
/℃
|
淬火温度/
℃及冷却
|
回火温度/℃或
去应力温度/℃
|
状态
|
σb
/MPa
|
σs
/MPa
|
δ5
(%)
|
硬度
HBS
|
| G-X70Cr29
|
1.4085
|
700~800
|
—
|
—
|
退火
|
880~900
|
—
|
—
|
210~280
|
| G-X120Cr29
|
1.4086
|
700~800
|
—
|
—
|
退火
|
880~1080
|
—
|
—
|
260~330
|
| G-X10CrMo13
|
1.4106
|
750~800
|
1000~10250
(空，水冷)
|
480~530
300~350
|
热处理
|
880~1030
|
735
|
8
|
265~310
|
| G-X70CrMo29 2
|
1.4136
|
700~800
|
—
|
—
|
退火
|
880~980
|
—
|
—
|
260~300
|
| G-X120CrMo29 2
|
1.4138
|
700~800
|
—
|
—
|
退火
|
880~1080
|
—
|
—
|
260~330
|
| G-X2CrNi18 9
|
1.4306
|
—
|
1050~1100
(空，水冷)
|
—
|
淬火
|
440~640
|
175
|
25
|
130~200
|
| G-X10CrNi18 8
|
1.4312
|
—
|
1030~1070
(空，水冷)
|
300~350
|
淬火
|
440~640
|
175
|
20
|
150~200
|
| G-X40CrNi27 4
|
1.4340
|
960~1000
(空，水冷)
|
—
|
—
|
退火
|
440~640
|
—
|
—
|
230~300
|
| G-X8CrNi26 7
|
1.4347
|
—
|
1030~1070
(空，水冷)
|
300~350
|
淬火
|
590~790
|
390
|
20
|
190~230
|
| G-X2CrNiMo18 10
|
1.4404
|
—
|
1050~1100
(空，水冷)
|
—
|
退火
|
440~640
|
185
|
25
|
130~300
|
| G-X5CrNiMo16 5
|
1.4405
|
—
|
1000~1050
(空，水冷)
|
580~620
|
热处理
|
760~960
|
540
|
15
|
240~300
|
| G-X10CrNiMo18 9
|
1.4410
|
—
|
1030~1070
(空，水冷)
|
300~350
|
淬火
|
440~640
|
185
|
20
|
130~200
|
| G-X6CrNiMo18 12
|
1.4437
|
—
|
1030~1070
(空，水冷)
|
300~350
|
淬火
|
440~640
|
185
|
20
|
130~200
|
| G-X2CrNiMo17 13 4
|
1.4446
|
—
|
1030~1070
(空，水冷)
|
350~400
|
淬火
|
490~640
|
205
|
20
|
150~200
|
| G-X6CrNiMo17 13
|
1.4448
|
—
|
1030~1070
(空，水冷)
|
350~400
|
淬火
|
440~640
|
185
|
20
|
130~200
|
| G-X6CrNiMo24 8 2
|
1.4463
|
—
|
1050~1100
(空，水冷)
|
—
|
退火
|
590~790
|
390
|
20
|
170~200
|
| G-X2CrNiMoN25 25
|
1.4405
|
—
|
1030~1070
(空，水冷)
|
350~400
|
淬火
|
440~640
|
185
|
25
|
130~200
|
| G-X2NiCrMoCuN20 18
|
1.4531
|
—
|
1030~1070
(空，水冷)
|
350~400
|
淬火
|
440~640
|
185
|
20
|
130~200
|
| G-X2NiCrMoCuN25 20
|
1.4536
|
—
|
1030~1070
(空，水冷)
|
350~400
|
淬火
|
440~640
|
180
|
20
|
130~200
|
| G-NiMo16CrW
|
2.4537
|
—
|
1200~1230
(空，水冷)
|
—
|
淬火
|
490~690
|
295
|
5
|
190~240
|
| G-X10CrNiMoNb18 12
|
1.4583
|
—
|
1030~1070
(空，水冷)
|
400~450
|
淬火
|
440~640
|
185
|
20
|
130~200
|
| G-X7CrNiMoCuNb18 18
|
1.4585
|
—
|
1050~1100
(空，水冷)
|
400~450
|
淬火
|
440~640
|
175
|
15
|
130~180
|
| G-NiMo30
|
2.4810
|
—
|
1175~1195
(空，水冷)
|
—
|
淬火
|
490~640
|
345
|
6
|
150~250
|
|
|
|
|
| 对应产品名：高锰铸钢和耐磨蚀铸钢
|
| 标准对照表：
|
|
|
| 标准内容：
|
| (1) 德国DIN标准高锰铸钢和耐磨蚀铸钢的钢号与化学成分[DIN SEW395-1998再确认]（表5-69）
表5-69 高锰铸钢和耐磨蚀铸钢的钢号与化学成分（质量分数）（%）
| 钢号
|
材料号
|
C
|
Si
|
Mn
|
P
≤
|
S
≤
|
Cr
|
Ni
|
Mo
|
其他
|
| G-X120Mn12
|
13401
|
1.10~1.30
|
0.30~0.50
|
12.0~13.0
|
0.100
|
0.040
|
≤1.50
|
—
|
—
|
—
|
| G-X110Mn14
|
13402
|
1.00~1.25
|
0.35~0.70
|
13.5~14.5
|
0.080
|
0.020
|
—
|
—
|
—
|
—
|
| G-X120Mn13
|
13802
|
1.1~1.3
|
≤0.50
|
11.5~13.5
|
0.060
|
0.030
|
≤0.50
|
—
|
—
|
—
|
| G-X25MnCrNi8 8 6
|
13966
|
0.22~0.28
|
≤0.70
|
7.5~9.5
|
0.045
|
0.030
|
7.0~8.5
|
5.0~6.0
|
—
|
—
|
| G-X12CrNi18 11
|
13955
|
≤0.15
|
≤1.0
|
≤2.0
|
0.045
|
0.030
|
16.5~18.5
|
10.0~12.0
|
≤0.75
|
—
|
| G-X2CrNiN18 13
|
13940
|
≤0.030
|
≤1.0
|
≤2.0
|
0.035
|
0.020
|
16.5~18.5
|
12.0~14.0
|
—
|
N0.10~0.20
|
| G-X2CrNiMoN18 14
|
13952
|
≤0.030
|
≤1.0
|
≤2.0
|
0.035
|
0.020
|
16.5~18.5
|
13.0~15.0
|
2.5~3.0
|
|
| G-X2CrNiMnMoNb21 16 5 3
|
13964
|
≤0.030
|
≤1.0
|
4.0~6.0
|
0.025
|
0.020
|
20.0~21.5
|
15.0~17.0
|
3.0~2.5
|
N0.25~0.35
Nb≤0.25
|
(2)德国DIN标准高锰铸钢和耐磨铸钢的力学性能（表5-70）
表5-70 高锰铸钢和耐磨铸钢的力学性能
| 钢 号
|
材料号
|
σb
/MPa
|
σ0.2
/MPa
|
δ5
(%)
|
AKV
/J
|
工作温度
/ ℃
|
| G-X120Mn13
|
1.3802
|
≥590
|
295
|
25
|
—
|
1000~1100
|
| G-X25MnCrNi8 8 6
|
1.3966
|
≥490
|
215
|
30
|
65
|
1050~1150
|
| G-X12CrNi18 11
|
1.3955
|
440~590
|
195
|
20
|
80
|
1050~1150
|
| G-X2CrNiN18 13
|
1.3940
|
440~640
|
210
|
30
|
115
|
1050~1150
|
| G-X2CrNiMoN18 14
|
1.3952
|
490~690
|
240
|
30
|
80
|
1050~1150
|
| G-X2CrNiMnMoNb21 16 5 3
|
1.3964
|
570~800
|
315
|
20
|
65
|
1050~1150
|
|
|
|
| 中国
GB1220-92[84]
GB3220-92[84]
|
日本
JIS
|
美国
AISI
UNS
|
英国
BS 970 Part4
BS 1449 Part2
|
德国
DIN 17440
DIN 17224
|
法国
NFA35-572
NFA35-576~582
NFA35-584
|
前苏联
TOCT5632
|
| 1Cr17Mn6Ni5N
|
SUS201
|
201
|
--
|
--
|
--
|
--
|
| 1Cr18Mn8Ni5N
|
SUS202
|
202
|
--
|
--
|
--
|
12×17.T9AH4
|
| --
|
--
|
S20200
|
284S16
|
--
|
--
|
--
|
| 2Cr13Mn9Ni4
|
--
|
--
|
--
|
--
|
--
|
--
|
| 1Cr17Ni7
|
SUS301
|
301
|
--
|
--
|
--
|
--
|
| --
|
--
|
S30100
|
301S21
|
X12CrNi177
|
Z12CN17.07
|
--
|
| 1Cr17Ni8
|
SUS301J1
|
--
|
--
|
X12CrNi177
|
--
|
--
|
| 1Cr18Ni9
|
SUS302
|
302
|
302S25
|
X12CrNi188
|
Z10CN18.09
|
12×18H9
|
| 1Cr18Ni9Si3
|
SUS302B
|
302B
|
--
|
--
|
--
|
--
|
| Y1Cr18Ni9
|
SUS303
|
303
|
303S21
|
X12CrNiS188
|
Z10CNF18.09
|
--
|
| Y1Cr18Ni9Se
|
SUS303Se
|
303Se
|
303S41
|
--
|
--
|
--
|
| 0Cr18Ni9
|
SUS304
|
304
|
304S15
|
X2CrNi89
|
Z6CN18.09
|
08×18B10
|
| 00Cr19Ni10
|
SUS304L
|
304L
|
304S12
|
X2CrNi189
|
Z2CN18.09
|
03×18H11
|
| 0Cr19Ni9N
|
SUS304N1
|
304N
|
--
|
--
|
Z5CN18.09A2
|
--
|
| 00Cr19Ni10NbN
|
SUS304N
|
XM21
|
--
|
--
|
--
|
--
|
| 00Cr18Ni10N
|
SUS304LN
|
--
|
--
|
X2CrNiN1810
|
Z2CN18.10N
|
|
| 1Cr18Ni12
|
SUS305
|
S30500
|
305S19
|
X5CrNi1911
|
Z8CN18.12
|
12×18H12T
|
| [0Cr20Ni10]
|
SUS308
|
308
|
--
|
--
|
--
|
--
|
| 0Cr23Ni13
|
SUS309S
|
309S
|
--
|
--
|
--
|
--
|
| 0Cr25Ni20
|
SUS310S
|
310S
|
--
|
--
|
--
|
--
|
| 0Cr17Ni12Mo2N
|
SUS315N
|
316N,S31651
|
--
|
--
|
--
|
--
|
| 0Cr17Ni12Mo2
|
SUS316
|
316
|
316S16
|
X5CrNiMo1812
|
Z6CND17.12
|
08×17H12M2T
|
| 00Cr17Ni14Mo2
|
SUS316L
|
316L
|
316S12
|
X2CrNiMo1812
|
Z2CND17.12
|
03×17H12M2
|
| 0Cr17Ni12Mo2N
|
SUS316N
|
316N
|
--
|
--
|
--
|
--
|
| 00Cr17Ni13Mo2N
|
SUS316LN
|
--
|
--
|
X2CrNiMoN1812
|
Z2CND17.12N
|
--
|
| 0Cr18Ni12Mo2Ti
|
--
|
--
|
320S17
|
X10CrNiMo1810
|
Z6CND17.12
|
--
|
| 0Cr18Ni14Mo2Cu2
|
SUS316J1
|
--
|
--
|
--
|
--
|
--
|
| 00Cr18Ni14Mo2Cu2
|
SUS316J1L
|
--
|
--
|
--
|
--
|
--
|
| 0Cr18Ni12Mo3Ti
|
--
|
--
|
--
|
--
|
--
|
--
|
| 1Cr18Ni12Mo3Ti
|
--
|
--
|
--
|
--
|
--
|
--
|
| 0Cr19Ni13Mo3
|
SUS317
|
317
|
317S16
|
--
|
--
|
08X17H15M3T
|
| 00Cr19Ni13Mo3
|
SUS317L
|
317L
|
317S12
|
X2CrNiMo1816
|
--
|
03X16H15M3
|
| 0Cr18Ni16Mo5
|
SUS317J1
|
--
|
--
|
--
|
--
|
--
|
| 0Cr18Ni11Ti
|
SUS321
|
321
|
--
|
X10CrNiTi189
|
Z6CNT18.10
|
08X18H10T
|
| 1Cr18Ni9Ti
|
--
|
--
|
--
|
--
|
--
|
12X18H20T
|
| 0Cr18Ni11Nb
|
SUS347
|
347
|
347S17
|
X10CrNiNb189
|
Z6CNNb18.10
|
08X18H12B
|
| 0Cr18Ni13Si4
|
SUSXM15J1
|
XM15
|
--
|
--
|
--
|
--
|
| 0Cr18Ni9Cu3
|
SUSXM7
|
XM7
|
--
|
--
|
Z6CNU18.10
|
--
|
| 1Cr18Mn10NiMo3N
|
--
|
--
|
--
|
--
|
--
|
--
|
| 1Cr18Ni12Mo2Ti
|
--
|
--
|
320S17
|
X10CrNiMoTi1810
|
Z8CND17.12
|
--
|
| 00Cr18Ni5Mo3Si2
|
--
|
S31500
|
--
|
3RE60(瑞典)
|
--
|
--
|
| 0Cr26Ni5Mo2
|
SUS329J1
|
--
|
--
|
--
|
--
|
--
|
| 1Cr18Ni11Si4AlTi
|
--
|
--
|
--
|
--
|
--
|
--
|
| 1Cr21Ni5Ti
|
--
|
--
|
--
|
--
|
--
|
--
|
| 0Cr13
|
SUS410S
|
S41000
|
--
|
X7Cr13
|
Z6C13
|
08X13
|
| 1Cr13
|
SUS410
|
410
|
410S21
|
X10Cr13
|
Z12Cr13
|
12X13
|
| 2Cr13
|
SUS420J1
|
420
|
420S29
|
X20Cr13
|
Z20Cr13
|
30X13
|
| --
|
--
|
S4200
|
420S27
|
--
|
--
|
--
|
| 3Cr13
|
SUS420J2
|
--
|
420S45
|
--
|
--
|
14X17H2
|
| 3Cr13Mo
|
--
|
--
|
--
|
--
|
--
|
--
|
| 3Cr16
|
SUS429J1
|
--
|
--
|
--
|
--
|
--
|
| 1Cr17Ni2
|
SUS431
|
431
|
431S29
|
X22CrNi17
|
Z15CN-02
|
--
|
| 7Cr17
|
SUS440A
|
440A
|
--
|
--
|
--
|
--
|
| 11Cr17
|
SUS440C
|
440C
|
--
|
--
|
--
|
95X18
|
| 8Cr17
|
SUS440B
|
44013
|
--
|
--
|
--
|
--
|
| 1Cr12
|
--
|
--
|
--
|
--
|
--
|
--
|
| 4Cr13
|
SUS420J2
|
--
|
--
|
X4DCr13
|
Z40C13
|
--
|
| 9Cr18
|
SUS440C
|
440C
|
--
|
X105CrMo17
|
Z100CD17
|
--
|
| 9Cr18Mo
|
SUS440C
|
440C
|
--
|
--
|
--
|
--
|
| 9Cr18MoV
|
SUS440B
|
440B
|
--
|
X90CrMoV18
|
Z6CN17.12
|
--
|
| 0Cr17Ni4Cu4Nb
|
SUS630
|
630
|
--
|
--
|
--
|
--
|
| 0Cr17Ni7Al
|
SUS631
|
631
|
--
|
--
|
--
|
09X17H710
|
| --
|
--
|
S17700
|
--
|
X7CrNiAl177
|
Z8CNA17.7
|
--
|
| 0Cr15Ni7Mo2Al
|
--
|
632
|
--
|
--
|
--
|
--
|
| --
|
--
|
S15700
|
--
|
--
|
Z8CND15.7
|
--
|
| 00Cr12
|
SUS410
|
--
|
--
|
--
|
--
|
--
|
| 0Cr13Al[00Cr13Al]
|
SUS405
|
405
|
--
|
--
|
--
|
--
|
| --
|
--
|
S40500
|
405S17
|
X7CrAl13
|
Z6CA13
|
--
|
| 1Cr15
|
SUS429
|
429
|
--
|
--
|
--
|
--
|
| 1Cr17
|
SUS430
|
430
|
--
|
--
|
--
|
12X17
|
| --
|
--
|
S43000
|
430S15
|
X8Cr17
|
Z8C17
|
--
|
| [Y1Cr17]
|
SUS430F
|
430F
|
--
|
--
|
--
|
--
|
| --
|
--
|
S43020
|
--
|
X12CrMoS17
|
Z10CF17
|
--
|
| 00Cr17
|
SUS430LX
|
--
|
--
|
--
|
--
|
--
|
| 1Cr17Mo
|
SUS434
|
434
|
--
|
--
|
--
|
--
|
| --
|
--
|
S43400
|
434S19
|
X6CrMo17
|
Z8CD17.01
|
--
|
| 00Cr17Mo
|
SUS436L
|
--
|
--
|
--
|
--
|
--
|
| 00Cr18Mo2
|
SUS444
|
--
|
--
|
--
|
--
|
--
|
| 00Cr27Mo
|
SUSXM27
|
XM27
|
--
|
--
|
--
|
--
|
| --
|
--
|
S44625
|
--
|
--
|
Z01CD26.1
|
--
|
| 00Cr30Mo2
|
SUS447J1
|
--
|
--
|
--
|
--
|
--
|
| 1Cr12
|
SUS403
|
403,S40300
|
403S17
|
--
|
--
|
--
|
| 1Cr13Mo
|
SUS410J1
|
--
|
--
|
--
|
--
|
--
|
|
|
|
| |
|
|
|